Drizoro - Maxrite S filling mortar
Price on request
Product description
Maxrite S is a PCC / SPCC filling mortar for repairing a hole in concrete. It is available as a one-component, fine-grained cement-polymer product with microsilica, to be mixed only with water. It has thixotropic properties, thanks to which it allows application up to 5 cm in one layer.
Technical data
- maximum grain size 3 mm
- dry mix density 1.3 0.1 g / cm 3
- mixing with water (by weight) 14 2%
- application setting time (at 20 ° C) initial 3-4 hours; final 7-8 hours
- the density of the hardened mortar 2.0 0.1 g / m 3
- compressive strength after 28 days (EN 12190) from 45 MPa
- ion content in chloride (UNE-EN 1015-17: 2001) up to 0.05%
- adhesion to the substrate (EN1542) from 2.0 MPa
- modulus of elasticity (EN 13142) from 20 GPa
- resistance to carbonation (EN13295) up to 4.0 mm
- capillary absorption (EN 13057) up to 0.5 kg / m 2 h 0.5
- fire resistance class A 1
- adhesion after freeze-thaw cycles (EN 13687-1) from 2.0 MPa
- adhesion after wetting cycles (EN 13687-2) from 2.0 MPa
- adhesion after drying cycles (EN 13687-4) from 2.0 MPa
- layer thickness minimum / maximum 5/50 mm
- consumption 1.7 0.1 kg / m 2 / mm
Application
- concrete repair
- concrete replenishment
- leveling concrete
- hydrotechnical and bridge structures
- increasing the thickness of the floors
- protection against carbonation
- resistance to frost and defrosting salts
- water vapor diffusion
- resistance to mechanical stress
Maxrite S can be applied by hand or by dry and wet spraying technology. Non-toxic product.