Drizoro - self-leveling mortar for Maxepox Floor floor systems
Price on request
Product description
Solvent-free, two-component epoxy binder recommended for floor systems with high mechanical and chemical properties for the protection and decorative finish of concrete and mortar.
Features
- due to its high abrasion resistance, it is suitable for heavy vehicular traffic
- very good resistance to chemicals: oils, greases, gasoline, acids and alkaline solutions, solvents, salts, etc.
- very good adhesion to concrete and mortar
- provides a continuous, uniform and consistent surface, with a non-slip finish
- easy to clean and maintain
- wide range of applications
- non-toxic, solvent-free and non-flammable
- quick maturation and putting into service
Application
- high abrasion resistance of the coating
- anti-skid multi-layer system with aggregate
- self-leveling system with high mechanical and chemical properties in garages, warehouses, sports halls, etc.
Technical data
- appearance and color of component A colored, homogeneous paste
- the appearance and color of component B is a clear, yellowish liquid
- Component ratio in A: B (weight) 4: 1
- component w proportions for A + B: C self-leveling mortar (to the weight) 1: 1 component w proportions for a dry mortar A + B: C (to the weight) 1: 3
- solids content component in A + B + C 100%
- component density in A + B 1.45 0.1 g / cm 3
- density for self-leveling mortar / dry mortar 1.90 / 2 0.1 g / cm 3
- flammability of the product non-flammable
- application and maturation temperature T / RH 8-30 C /> 85%
- shelf life at 10 C / 20 C / 30 C - 45/30/10 min
- drying time at 20 C 6–8 h
- time between the planes at 20 ° C 6-24 h
- maturing time at 20 ° C: 1 days for pedestrian traffic; for high beam 3 days; for heavy vehicle traffic 4 days
- bending strength for 28 days 32.6 MPa (according to EN 13892-2)
- compressive strength for 28 days 61.0 MPa (according to EN 13892-2)
- adhesion to concrete for 28 days> 3 MPa (according to EN 13892-2)
- consumption / thickness: applied as a clean surface - consumption for one coat / total application 0.25-0.3 / 0.5-0.6 kg / m 2 ; - thickness per coat / total application 170–200 / 340–400 kg / m 2 ; applied as an emitted multilayer system - total estimated consumption for resin A + B / aggregate C 1.0–1.2 / 1.0–1.5 kg / m 2 - recommended thickness 1–2 mm; applied as a self-leveling mortar - expected consumption 2.0 kg / m 2 mm of thickness - recommended thickness for a layer 1–2 mm; applied as a dry mortar: consumption 2.0 kg / m 2 mm of thickness - recommended thickness for a layer of 2-10 mm
- package 25 kg