Drizoro - mortar for filling joints and working cracks Maxjoint Elastic
Price on request
Product description
A two-component mortar, where component A is a liquid based on special synthetic resins, and component B is delivered in the form of a powder, based on a mixture of cement, an addition of and specially selected aggregate. After mixing the two components, a resin-cement product with high adhesion is obtained, suitable for sealing and filling joints susceptible to movement and cracks in concrete.
Features
- allows to achieve a joint displacement capacity of up to 15%
- very high resistance and resistance to weather conditions
- does not require maintenance
- excellent adhesion to wet surfaces
- does not require a tack coat
- does not run off vertical surfaces
- suitable for permanent contact with drinking water, waterproof
- easy to apply and finish
- non-toxic, non-flammable and environmentally friendly product
- after setting, it can be painted in the desired color
Application
- repair of cracks prone to movement, cracks in concrete and masonry structures
- sealing of working cracks, cracks, expansion joints with deformability up to 15%; working cracks, cracks, gaps constantly immersed in water: pipelines, water tanks, tanks of sewage treatment plants, etc., gaps in prefabricated elements in concrete, ceramic on facades and structures
- as a mortar for pointing flexible surfaces
- as a flexible sealing, filling of expansion gaps in bridge structures
- as a flexible seal, filling gaps between curbs
Technical data
- appearance of component A milky white liquid
- component B appearance gray powder
- component A density 1.0 0.05 g / cm 3
- Density of component B 0.9 0.05 g / cm 3
- maximum size of the aggregate 0.4 mm
- Component ratio in A: B (by weight) 1: 1
- density of A + B fresh mix 1.26 0.05 g / cm 3
- the density of the mature A + B mixture 1.14 0.05 g / cm 3
- time to build in at 20 C about 30 min
- optimal application temperature 5–30 C
- A + B shelf life 30-60 min
- joint deformation 15%
- tensile strength 0.38 MPa (according to EN 28339)
- elongation at break 60% (according to EN 28339)
- deformation recovery 78% (according to EN 27389)
- package 10 kg